Pengamatan Atas Daerah Interface Pada Cladding Material Stainless Steel Terhadap Baja Karbon Rendah Secara Metalografi dan Uji Keras

  • Yohanes Hutahaean Mahasiswa Universitas HKBP Nommensen
  • Sahat Mauli Lubis Mahasiswa Universitas HKBP Nommensen
  • Charles Manurung Universitas HKBP Nommensen
  • Salomo Simanjuntak Universitas HKBP Nommensen
  • Yetty R Saragi Universitas HKBP Nommensen
DOI: https://doi.org/10.36655/sproket.v2i2.527
Keywords: Cladding, Heating Temperature, Stainless Steel, Low Carbon Steel, Emphasis, Hardness Test and Microstructure

Abstract

Low carbon steel metal is a type of steel that has poor corrosion resistance. For that it is necessary to protect against corrosion through a coating process. In this case the coating is carried out using solid metal and is known as cladding. In this cladding process using another metal as a coating medium, namely stainless steel, the specimen will be given additional deformation from the outside in the form of pressure and the heating process is carried out above the recrystallization temperature (950oC) then cooled slowly in free air. The heating process of the specimens was carried out with three temperature variations, namely 750oC, 850oC and 950oC with a holding time of 60 minutes, from the research results obtained that the specimens and the highest temperature, 950 oC, had better metal bonds compared to specimens at temperatures of 750 and 850oC with hardness values. average 227.96 VHN.

References

1. Callister Jr,William D, 2007, Material and Engineering, An Introduction, sixth edition, Jhon Wiley & Son. Inc
2. ASM Handbook , Surface Engineering, Vol 5
3. Hopkins, D.W., Principles of Metal Surface Treatment and Protection, Pergamon International Library, Second Edition, 2005.
4. Dian Yezhi Anggoro, Samsudi Raharjo, Solechan, “Pengaruh Pack carburizing dengan Arang Batok Kelapa Terhadap Kekerasan Roda Gigi Fly Wheel Daihatsu” Majalah Ilmiah Teknik TRAKSI Vol. 13 No.1. 2013.
5. Adi Dermawan, Mustaqim, Fajar Sidiq, “Pengaruh Temperatur Carburizing Pada Proses Pack Carburizing Terhadap Sifat - Sifat Mekanis Baja S21C” Jurnal Engineering, Vol. 14 No. 1., 2017.
6. Muhammad Zuchry M. , “Pengaruh Karburasi Dengan Variasi Media Pendingin Terhadap Micro Struktur Baja Karbon”, majalah Ilmiah MEKTEK, Tahun XIII NO. 2, Mei 2011
7. Wiskocil Davis Troxell, “The Testing and Inspection Of Engineering Materials”, Third Edition, 2001
8. George F. Vander Voord, “Metallography, Principles and Practice”, Vol 36 , Mc. Graw Hill, 1984
Published
2021-02-26
How to Cite
Hutahaean, Y., Lubis, S., Manurung, C., Simanjuntak, S., & Saragi, Y. (2021). Pengamatan Atas Daerah Interface Pada Cladding Material Stainless Steel Terhadap Baja Karbon Rendah Secara Metalografi dan Uji Keras. SPROCKET JOURNAL OF MECHANICAL ENGINEERING, 2(2), 72-86. https://doi.org/https://doi.org/10.36655/sproket.v2i2.527
Issue
Vol 2 No 2 (2021): Edisi Februari 2021
Section
Articles
Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.

Authors who publish with  SPROCKET JOURNAL OF MECHANICAL ENGINEERING agree to the following terms:

  • Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution 4.0 International License . that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
  • Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.
  • Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).