Analisa Laju Korosi dan Kekerasan Pada Stainless Steel 316 L Dalam Larutan 10 % NaCl Dengan Variasi Waktu Perendaman

  • Arga Jeremia Sinaga Universitas HKBP Nommensen
  • Charles Manurung Universitas HKBP Nommensen
DOI: https://doi.org/10.36655/sprocket.v1i2.186
Keywords: corrosion rate, hardness, 316L, 10% NaCl, soaking time

Abstract

Corrosion is an electrochemical reaction between metals and the environment that causes corrosion and decreases the quality of metals. Steel is a metal material that is widely applied in the industrial world. Stainless steel is stainless steel that is resistant to corrosion because it has an alloying element of at least 18% chrome and 8% nickel. To find out the superiority of stainless steel as a construction material, research on local corrosion of stainless steel needs to be done. For this reason, research on corrosion is carried out by using a 10% NaCl salt solution by varying the immersion time of stainless steel in corrosive media. From the research results it is known that the type of corrosion that occurs in specimens is the type of uniform corrosion. Likewise with the value of violence will decrease if the stainless steel is soaked longer.

References

1. Yudha Kurniawan Afandi, Irfan Syarif Arief, dan Amiadji, Analisa Laju Korosi pada Pelat Baja Karbon dengan Variasi Ketebalan Coating, JURNAL TEKNIK ITS Vol. 4, No. 1, (2015)
2. Djoko Hadi Pratikno, Jan Setiawan, Elektrokimia Baja Tahan Karat SS 316 Dalam Media Nano Fluida, Jurnal Urania Vol. 25 No. 1, Februari 2019: 1−70
3. I.G. Ayu Arwati, Edy Herianto Majlan, Wan Ramli Wan Daud, Loh Kee, Temperature Effects on Stainless Steel 316L Corrosion in the Environment of Sulphuric Acid (H2SO4), IOP Conf. Series: Materials Science and Engineering 343 (2018)
4. R. Kohar, Laju dan bentuk korosi pada baja karbon menengah yang mendapat perlakuan pada suhu austenite diuji di dalam larutan NaCl 3 N, Jurnal Desiminasi Teknologi, Volume 1, Nomor 1, Januari 2013
5. Afriwan Wahyu Pratama, Paridawati, Tri Santoso, Analisa laju korosi dan struktur mikro terhadap baja karbon rendah SS400 pada metode pelapisan hot dip galvanizing, Prosiding Seminar Nasional Energi dan Teknologi, UNISMA BEKASI, Juni 2019.
6. Wahyu Kheren Sabyantoro, Helmy Purwanto dan Muhammad Dzulfikar, Analisis laju korosi dengan aliran media korosi HCL 10% pada material baja ASTM A36 dengan sudut bending, Momentum, Vol. 15, No. 1, April 2019
Published
2020-03-14
How to Cite
Sinaga, A., & Manurung, C. (2020). Analisa Laju Korosi dan Kekerasan Pada Stainless Steel 316 L Dalam Larutan 10 % NaCl Dengan Variasi Waktu Perendaman. SPROCKET JOURNAL OF MECHANICAL ENGINEERING, 1(2), 92-99. https://doi.org/https://doi.org/10.36655/sprocket.v1i2.186
Issue
Vol 1 No 2 (2020): Edisi Februari 2020
Section
Articles

Penulis yang menerbitkan dengan  SPROCKET JOURNAL OF MECHANICAL ENGINEERING menyetujui ketentuan berikut :

  • Penulis memegang hak cipta dan memberikan jurnal hak penerbitan pertama dengan karya yang dilisensikan secara bersamaan di bawah Lisensi Internasional Creative Commons Atribusi 4.0 . yang memungkinkan orang lain untuk berbagi karya tersebut dengan pengakuan atas kepengarangan karya dan penerbitan awal dalam jurnal ini.
  • Penulis dapat membuat pengaturan kontraktual tambahan yang terpisah untuk distribusi non-eksklusif atas versi jurnal yang diterbitkan dari suatu karya (misalnya, mempostingnya ke repositori institusional atau menerbitkannya dalam sebuah buku), dengan pengakuan atas penerbitan awalnya di jurnal ini.
  • Penulis diizinkan dan didorong untuk mengunggah karya mereka secara daring (misalnya, di repositori institusi atau di situs web mereka) sebelum dan selama proses penyerahan, karena hal ini dapat mengarah pada pertukaran yang produktif, serta kutipan yang lebih awal dan lebih banyak dari karya yang diterbitkan (Lihat  Pengaruh Akses Terbuka ).