Besarnya Penyusutan Yang Terjadi Pada Peleburan Logam Non-Fero Dengan Menggunakan Bahan Baku 2.5 Ton Logam Untuk Pembuatan Komponen Boiler Pada Tanur Kupola Di PT. X

AMOUNT OF SHRINKAGE THAT OCCURS IN THE MELTING OF NON-FERROUS METALS USING 2.5 TONS OF METAL AS RAW MATERIALS FOR THE MANUFACTURE OF BOILER COMPONENTS AT CUPOLA FURNACE IN PT. X

  • Herry Darmadi Politeknik Teknologi Kimia Industri Medan
  • Muhammad Andika Dewatmoko Politeknik Teknologi Kimia Industri Medan
  • Dian Kurnia Politeknik Teknologi Kimia Industri Medan
  • Nurul Shadrina Bintang Politeknik Teknologi Kimia Industri Medan
DOI: https://doi.org/10.36655/sprocket.v7i1.1932
Keywords: smelting, non-ferrous, coke, metal, carbon

Abstract

The casting industry is a kind of mining industry, where all industry manufacturing would never exist without the casting of the casting industry, much more difficult for the economy of a country without its own industrial role. A brushwork furnace that is one of the most popular types of metal smelting kitchens. The large shrink that occurs at smelting metals for making boiler components using 2.5 tons of raw materials is 15.08 percent or weighing 2,123 kg. the foundry in PT X using cocash-fuel (coal with high carbon levels). The process of smelting metals included sand prints that served the desired components, supplying raw materials and fuel to suit needs, smelting the kiln in my furnace with the help of blowers, pouring the molten metal into the ground, and cooling the molten metal.

References

[1] A. Sudiyanto and N. A. Shiddiq, "Proses Pengecoran Logam Dan Analisa Cacat," Journal of Metallurgical Engineering and Processing Technology, vol. 1, no. 1, 2020.
[2] S. Tjitro and L. S. Hartanto, "Pengaruh Modulus Cor Riser Terhadap Cacat Penyusutan Pada Produk Paduan Al-Si," Jurnal Teknik Mesin, vol. 4, no. 2, 2004.
[3] X. Yang, X. Chen, T. Zhang, J. Ye, G. Lv and a. Zhang, "Study on Reductive Smelting of High-Iron Red Mud for Iron Recovery," MDPI, vol. 12, no. 4, 2022.
[4] K. Gunawan, K. D. Yuliawan, A. T. Hartanto and I. G. S. Sudaryana, "Perancangan Dan Pembuatan Tungku Peleburan Logam Untuk Menunjang Kegiatan Praktikum Dan Penelitian Di Laboratorium Manufaktur," Jurnal Pendidikan Teknik Mesin Undiksha, vol. 11, no. 1, 2023.
[5] D. AMALIA and M. AZIZ, "Percobaan Pendahuluan Pembuatanalumina Kualitas Metalurgi Dari Bauksitkalimantan Bara," Jurnal Teknologi Mineral dan Batubara, vol. 7, no. 4, pp. 183-191, 2011.
[6] E. Herianto and R. Binudi, "Kupola Udara Panas Untuk Memproduksi NPI (Nickel Pig Iron) Dari Bijih Nikel Laterit. Majalah Metalurgi," Majalah Metalurgi, vol. 28, no. 2, pp. 121-130, 2019.
[7] D. Kusumawaty, H. Pardosi, P. Sitindaon and J. G. Simanjuntak, "Modifikasi Tanur Kupola.," Jurnal Teknik dan Teknologi, vol. 15, no. 30, 2020.
[8] E. Ghassemali, A. E. W. Jarfors and A. DiószegiORCID, "On the Formation of Micro-Shrinkage Porosities in Ductile Iron Cast Components," MDPI, vol. 8, no. 7, 2018.
Published
2025-08-28
How to Cite
Darmadi, H., Dewatmoko, M., Kurnia, D., & Bintang, N. (2025). Besarnya Penyusutan Yang Terjadi Pada Peleburan Logam Non-Fero Dengan Menggunakan Bahan Baku 2.5 Ton Logam Untuk Pembuatan Komponen Boiler Pada Tanur Kupola Di PT. X. SPROCKET JOURNAL OF MECHANICAL ENGINEERING, 7(1), 27-34. https://doi.org/https://doi.org/10.36655/sprocket.v7i1.1932
Issue
Vol 7 No 1 (2025): Edisi Agustus 2025
Section
Articles
Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.

Penulis yang menerbitkan dengan  SPROCKET JOURNAL OF MECHANICAL ENGINEERING menyetujui ketentuan berikut :

  • Penulis memegang hak cipta dan memberikan jurnal hak penerbitan pertama dengan karya yang dilisensikan secara bersamaan di bawah Lisensi Internasional Creative Commons Atribusi 4.0 . yang memungkinkan orang lain untuk berbagi karya tersebut dengan pengakuan atas kepengarangan karya dan penerbitan awal dalam jurnal ini.
  • Penulis dapat membuat pengaturan kontraktual tambahan yang terpisah untuk distribusi non-eksklusif atas versi jurnal yang diterbitkan dari suatu karya (misalnya, mempostingnya ke repositori institusional atau menerbitkannya dalam sebuah buku), dengan pengakuan atas penerbitan awalnya di jurnal ini.
  • Penulis diizinkan dan didorong untuk mengunggah karya mereka secara daring (misalnya, di repositori institusi atau di situs web mereka) sebelum dan selama proses penyerahan, karena hal ini dapat mengarah pada pertukaran yang produktif, serta kutipan yang lebih awal dan lebih banyak dari karya yang diterbitkan (Lihat  Pengaruh Akses Terbuka ).