Analisa Pengaruh Pendingin Terhadap Struktur Mikro Dan Sifat Mekanik Pada Baja ST 60
Abstract
The field of industry that produces human needs is growing rapidly. Encouraging increased productivity with iron metal-based machine components. Using quality materials, and certified. This research uses ST 60 steel with a carbon content of 0.48%.. The research process that will be carried out is Heat treatment is needed to minimize failure, change the structure, and form the desired properties, the rapid cooling process to produce a comparison of hardness in material variations, hardness testing to determine the hardness of a material, and observation of microstructure to observe the type of microstructure formed after heat treatment and without heat treatment. After testing, the heat treatment process greatly affects changes in the mechanical properties of the material, as evidenced by the increase in hardness values which initially before the heat treatment process amounted to 194.6 Kgrf / to 255.53 Kgrf / with SAE 40 lubricant cooling media, 220.43 Kgrf / with 50% lubricant cooling media with 50% water mixture, and 300, 7 Kgrf/ with long life coolant media and it is proven that in each material given heat treatment the hardness value has increased as well, before heat treatment the hardness value in ST 60 steel is only 194.6 Kgrf/, experiencing an increase in mechanical properties, namely work with SAE 40 lubricant cooling media with a value of 255.53 Kgrf/, 50% lubricant cooling media with 50% water mixture worth 220.43 Kgrf/ and long life coolant of 300.7 Kgrf/.
References
[2] B. Agung Permana, M. Badaruddin, and dan Zulhanif, “Juli 2013) 1) Mahasiswa Jurusan Teknik Mesin, Fakultas Teknik Universitas Lampung 2) Dosen Jurusan Teknik Mesin, Fakultas Teknik Universitas Lampung Jln.”
[3] Murtiono, Arief. 2012. “Pengaruh Quenching dan Tempering Terhadap Kekerasan dan Kekuatan Tarik Serta Struktur Mikro Baja Karbon Sedang Untuk Mata Pisau Pemanen Sawit’’. Jurnal E-Dinamis, Vol. 3, No. 2. Hal. 58-59.
This work is licensed under a Creative Commons Attribution 4.0 International License.
Penulis yang menerbitkan dengan SPROCKET JOURNAL OF MECHANICAL ENGINEERING menyetujui ketentuan berikut :
- Penulis memegang hak cipta dan memberikan jurnal hak penerbitan pertama dengan karya yang dilisensikan secara bersamaan di bawah Lisensi Internasional Creative Commons Atribusi 4.0 . yang memungkinkan orang lain untuk berbagi karya tersebut dengan pengakuan atas kepengarangan karya dan penerbitan awal dalam jurnal ini.
- Penulis dapat membuat pengaturan kontraktual tambahan yang terpisah untuk distribusi non-eksklusif atas versi jurnal yang diterbitkan dari suatu karya (misalnya, mempostingnya ke repositori institusional atau menerbitkannya dalam sebuah buku), dengan pengakuan atas penerbitan awalnya di jurnal ini.
- Penulis diizinkan dan didorong untuk mengunggah karya mereka secara daring (misalnya, di repositori institusi atau di situs web mereka) sebelum dan selama proses penyerahan, karena hal ini dapat mengarah pada pertukaran yang produktif, serta kutipan yang lebih awal dan lebih banyak dari karya yang diterbitkan (Lihat Pengaruh Akses Terbuka ).
.png)
.png)